牌号
Trade
Mark

主要成份(%)
Chemical
Composition

特性和用途
Characteristics &
Application

相当AWS
Equivalent to
AWS

S201

Sn1 Si0.3 Mn0.3
Cu Rem

机械性能好，抗裂性能好。紫铜气焊及氩弧焊用。
to gas weld or argon arc weld red copper, and to get good mechanical properties and cracking resistance

ERCu

S211

Si3 Mn1 Cu Rem

机械性能好。铜合金氩弧焊及钢的MIG钎焊用。
to gas weld copper alloy or to MIG weld steel, and to get good mechanical properties

ERCuSi-A

S212

Sn5 P0.2 Cu Rem

耐磨性好。铜合金氩弧焊及钢的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear

ERCuSn-A

S213

Sn8 P0.2 Cu Rem

耐磨性好。铜合金氩弧焊及钢的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear

ERCuSn-C

S214

Al7.5 Cu Rem

耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion

ERCuAl-A1

S215

Al9 Cu Rem

耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用。
to argon arc weld copper alloy or to resurface steel, and to get good resistance to wear and corrosion

ERCuAl-A2

S221

Cu60 Sn1 Si0.3
Zn Rem

熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁。
melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well

S221F

Cu60 Sn1 Si0.3
Zn Rem

外涂焊剂的S221焊丝。
S221 welding rod coated with flux

S222

Cu58 Sn0.9 Si0.1
Fe0.8 Zn Rem

熔点约890℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁。
melt at about 890℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well

RBCuZn-C

S222F

Cu58 Sn0.9 Si0.1
Fe0.8 Zn Rem

外涂焊剂的S222焊丝。
S222 welding rod coated with flux

RBCuZn-C

S223

Cu59 Sn0.6 Zn Rem

熔点约900℃。铜、钢、铸铁钎焊用。
melt at about 900℃ to braze weld copper, steel or cast iro

RBCuZn-A

S224

Cu62 Si0.5 Zn Rem

熔点约905℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁。
melt at about 905℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well

S225

Cu48 Ni10 Zn Rem

熔点约935℃。高强度，钎焊钢、镍及硬质合金用。
melt at about 935℃ to braze weld steel, nickel or kentanium, and to get high strength

RBCuZn-D

S225F

Cu48 Ni10 Zn Rem

外涂焊剂的S225焊丝。
S225 welding rod coated with flux

RBCuZn-D

S226

Cu60 Sn0.3 Si0.2
Zn Rem

熔点约900℃。黄铜气焊用，也可钎焊铜、钢、铸铁。
melt at about 900℃ to gas weld bronze copper, and to braze weld copper, steel or cast iron as well

S227

Cu58 Sn0.9 Ni0.5
Si0.1 Fe0.8 Zn Rem

熔点约880℃。黄铜气焊及碳弧焊用，也可钎焊铜、钢、铸铁。
melt at about 880℃ to gas weld or carbon arc weld bronze copper, and to braze weld copper, steel or cast iron as well

RBCuZn-B

S229

Cu55 Ni6 Mn4
Zn Rem

熔点约920℃。高强度，钎焊钢、镍及硬质合金用。
melt at about 920℃ to braze weld steel, nickel or kentanium, and to get high strength

牌号
Trade
Mark

主要成份(%)
Chemical
Composition

特性和用途
Characteristics &
Application

相当AWS
Equivalent to
AWS

S301

SAl 1070

塑性好、耐蚀。纯铝气焊、氩弧焊用。
to gas weld or argon arc weld aluminum, and to get good ductility and resistance to corrosion

ER1070

ER4043

SAl 4043
(S311)

抗裂性好、通用性大。铝合金气焊、氩弧焊用。不宜用于铝镁合金。
with a wide range of usage to gas weld or argon arc weld aluminum alloy except magaluma, and to get good cracking resistance

ER4043

ER5183

SAl 5183

耐蚀、强度高。铝合金氩弧焊用。
to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength

ER5183

ER5356

SAl 5356

耐蚀、强度高，通用性大。铝合金氩弧焊用。
with a wide range of usage to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength

ER5356

ER5556

SAl 5556
(S331)

耐蚀、强度高。铝合金氩弧焊用。
to argon arc weld aluminum alloy, and to get resistance to corrosion and high strength

ER5566

牌号
Trade
Mark

主要成份(%)
Chemical
Composition

特性和用途
Characteristics &
Application

相当AWS
Equivalent to
AWS

S111

C1 Cr29 W5
Co Rem

HRc=40~45，高温下耐磨、耐蚀。堆焊高温高压阀门。
apply to resurface and to get resistance to wear and corrosion at high temperature

RCoCr-A

S112

C1.5 Cr29 W8
Co Rem

HRc=45~50，高温下耐磨、耐蚀。堆焊阀门、热轧孔型。
apply to resurface and to get resistance to wear and corrosion at high temperature

RCoCr-B

S114

C2.5 Cr30 W12
Co Rem

HRc52，高温下耐磨、耐热，但抗冲击性较差。堆焊牙轮钻头。
apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance

RCoCr-C

S190

C3.2 Cr27 W14
Co Rem

HRc55，高温下耐磨、耐热，但抗冲击性较差。堆焊牙轮钻头。
apply to resurface and to get resistance to wear and corrosion at high temperature, but poor in shock resistance

RCoCr-G